Covestro PC+ABS Bayblend T95 MF heat resistance
| Brand Name | Covestro |
| Model Number | T90 MF |
| Document | Bayblend T90 MF 20_en_56968...76.pdf |
Product Details
Payment & Shipping Terms
Minimum Order Quantity
25KG
Price
*USD to be negotiated
Packaging Details
25Kgs/BAG
Payment Terms
L/C, T/T, Western Union, MoneyGram
Product Description
General purpose grades
(PC+ABS)-Blend; 9 % mineral filled; Vicat/B 120 temperature = 142 °C;; very good heat resistance; reduced coefficient of thermal expansion; tensile modulus = 3350 MPa
Rheological
| Property | Test Condition | Unit | Standard | typical Value | |
| C | Melt volume-flow rate | 260 °C/ 5 kg | cm³/10 min | ISO 1133 | 18 |
|
Melt viscosity
|
1000 s-1/ 260 °C
|
Pa·s
|
b.o. ISO 11443-A
|
400
|
|
|
Molding shrinkage, parallel
|
150x150x3 mm/ 260 °C / MT 80 °C
|
% | b.o. ISO 2577 | 0.5 -0.7 | |
| Molding shrinkage, normal | 150x150x3 mm/ 260 °C / MT 80 °C | % | b.o. ISO 2577 | 0.5 -0.7 | |
Mechanical properties (23 °C/50 % r. h.)
| Property | Test Condition | Unit | Standard | typical Value | |
|---|---|---|---|---|---|
| C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 3350 |
| C |
Yield stress
|
50 mm/min | MPa | ISO 527-1,-2 | 66 |
| C | Yield stress | 50 mm/min | % | ISO 527-1,-2 | 4.6 |
|
Stress at break
|
50 mm/min | MPa | ISO 527-1,-2 |
52
|
|
|
Strain at break
|
50 mm/min | % | ISO 527-1,-2 | >=50 | |
|
Izod impact strength
|
23 °C | kJ/m² | ISO 180/U | >=150 | |
|
Izod notched impact strength
|
23 °C | kJ/m² | ISO 108/A | 9.0 | |
| Izod notched impact strength | -30 °C | kJ/m² | ISO 108/A | 9.0 | |
Resins wholesale,Factory-Direct supply,Certified supplier
Main Product: PC,PC/ABS,PC/PET,PC/PBT
Customized Services: Modified, Color matching, Production technical support
Several Warehouse: Guang zhou, Dong guan, Shen zhen, Hong kong
Get in Touch for More Info! and Speak to Our Manager Today!
Recommended Products
Contact Us at Any Time
+8618002579887
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong