Covestro Bayblend Products and Grades
| Brand Name | Covestro |
| Model Number | Pushing boundaries with advanced polycarbonate specialties |
Product Description
Bayblend® variants exhibit an exceptional balance of properties, most notably outstanding toughness – even under cold temperatures – along with considerable rigidity, remarkable dimensional stability, excellent creep resistance, low moisture absorption, notable heat resistance, and high flame retardancy.
Key Beneifits
 |
►Tough: Experience high toughness even at low temperatures. |
| Characteristic features | Processing and fabrication | Main areas of application |
|---|---|---|
|
Color
Dimensional accuracy
|
Processing the raw material Injection molding, extrusion, extrusion blow molding Secondary processing Thermoforming, e.g. by bending and stamping; cold forming, e.g. by high-pressure molding Machining Sawing, drilling, turning, milling, planing, grinding, tap-ping and die-cutting Jointing Screwing, bonding, welding and riveting Finishing Painting, printing, metallizing and laser marking |
|
Products List
| Code | Property | Grade |
| Bayblend® T45 PG | (ABS+PC)-blend; Vicat/B 120 temperature = 112 °C; for electroplating applications |
Non-reinforced general purpose grades |
| Bayblend® T50 XF | (PC+ABS)-blend; Vicat/B 120 temperature = 112 °C; excellent flow; good low temperature impact strength | |
| Bayblend® T65 AT | (PC+ABS)-blend; Vicat/B 120 temperature = 121 °C; improved antistatic behavior | |
| Bayblend® T65 HG | (PC+ABS)-blend; Vicat/B 120 temperature = 120 °C; easy flowing; high gloss; brilliant colors | |
| Bayblend® T65 PG | (PC+ABS)-blend; Vicat/B 120 temperature = 120 °C; easy flowing; good heat resistance; for electroplating applications | |
| Bayblend® T65 XF | (PC+ABS)-blend; Vicat/B 120 temperature = 120 °C; improved flow compared with T65 Bayblend® T80 XG (PC+ABS)-blend; Vicat/B 120 temperature = 130 °C; excellent flow; optimized surface quality for metallization (steam treatment) | |
| Bayblend® T65 HI | (PC+ABS)-blend; Vicat/B 120 temperature = 120 °C; grade with improved low-temperature impact strength and chemical resistance for automotive parts; also suitable for extrusion/extrusion blow molding and electroplating applications | |
| Bayblend® T85 HG | (PC+ABS)-blend; Vicat/B 120 temperature = 130 °C; easy flowing; high gloss; brilliant colors |
Non-reinforced general purpose grades |
| Bayblend® T85 SG | (PC+ABS)-blend; Vicat/B 120 temperature = 130 °C; very good flow; suitable for DirectCoating/DirectSkinning | |
| Bayblend® T85 XF | (PC+ABS)-blend; Vicat/B 120 temperature = 130 °C; improved flow compared with T85 | |
| Bayblend® T90 HT | (PC+ABS)-blend; high heat resistance; Vicat/B 120 temperature = 135 °C; easy flowing; ball indentation temperature >= 125 °C; suitable as supporting material for energized parts | |
| Bayblend® T90 XF | (PC+ABS)-blend; Vicat/B 120 temperature = 132 °C; good balance of melt flow, impact strength and stress cracking resistance | |
| Bayblend® T90 XG | (PC+ABS)-blend; Vicat/B 120 temperature = 135 °C; easy flowing; optimized surface quality for metallization (steam treatment) | |
| Bayblend® T88 GF-10 | Rubber modified (PC+SAN)-blend; 10 % glass fiber reinforced; Vicat/B 120 temperature = 134 °C; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 4,800 MPa; good heat resistance |
Glass fiber reinforced general purpose grades |
| Bayblend® T88 GF-20 | Rubber modified (PC+SAN)-blend; 20 % glass fiber filled; Vicat/B 120 temperature = 130 °C; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 7,200 MPa; good heat resistance | |
| Bayblend® T88 GF-30 | Rubber modified (PC+SAN)-blend; 31 % glass fiber filled; Vicat/B 120 temperature = 134 °C; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 10,000 MPa; good heat resistance | |
| Bayblend® T90 | MF-20 Rubber modified (PC+SAN)-blend; 20 % mineral filled; Vicat/B 120 temperature = 130 °C; very good flow; reduced coefficient of thermal expansion; tensile modulus = 4,900 MPa; good heat resistance |
Mineral filled general purpose grades |
| Bayblend® T95 | MF (PC+ABS)-blend; 9 % mineral filled; Vicat/B 120 temperature = 142 °C; very good heat resistance; reduced coefficient of thermal expansion; tensile modulus = 3,350 MPa |
Mineral filled general purpose grades |
| Bayblend® W85 HI | (PC+ASA)-blend; Vicat/B 120 temperature = 132 °C; easy flowing; improved weather resistance; excellent low temperature ductility; good heat resistance |
General purpose grades with improved weatherability |
| Bayblend® W85 XF | (PC+ASA)-blend; Vicat/B 120 temperature = 134 °C; improved weather resistance; excellent low temperature ductility; good heat resistance | |
| Bayblend® M850 XF | (PC+ABS)-blend; easy flowing; Vicat/B 120 temperature = 131 °C; meet certain requirements of ISO Standard 10993-1; for further information please contact plastics@covestro.com |
General purpose grades for medical application* |
| Bayblend® FR3000 | (PC+ABS)-blend; flame retardant; easy flowing; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 at 1.5 mm; glow wire test: 960 °C at 2.0 mm; no juicing; good light stability |
Non-reinforced flame retardant grades |
| Bayblend® FR3000 HI | (PC+ABS)-blend; flame retardant; Vicat/B 120 temperature = 97 °C; compared to FR3000 improved chemical resistance and stress cracking behavior; UL recognition 94 V-0 at 1.5 mm | |
| Bayblend® FR3005 HF | (PC+ABS)-blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96 °C; UL recognition 94 V-0 at 1.5 mm | |
| Bayblend® FR3008 HR | (PC+ABS)-blend; flame retardant; Vicat/B 120 temperature = 103 °C; improved chemical and very good hydrolysis resistance; HDT/A >= 85 °C; UL recognition 94 V-0 at 1.5 mm; glow wire test: 960 °C at 2.0 mm; good light stability | |
| Bayblend® FR3010 | (PC+ABS)-blend; flame retardant; Vicat/B 120 temperature = 110 °C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010 | |
| Bayblend® FR3010 HF | (PC+ABS)-blend; flame retardant; easy flowing; Vicat/B 120 temperature = 108 °C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °C at 2.0 mm; optimized processability; good light stability | |
| Bayblend® FR3010 IF | (PC+ABS)-blend; flame retardant; Vicat/B 120 temperature = 108 °C; increased heat resistance; UL recognition 94 5VB (1.5 mm); glow wire temperature (GWFI): 960 °C at 2.0 mm | |
| Bayblend® FR3011 | (PC+ABS)-blend; flame retardant; easy flowing; Vicat/B 120 temperature = 118 °C; good heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °C at 2.0 mm; good light stability | |
| Bayblend® FR3015 BBS910 | (PC+ABS)-blend; flame retardant; UV stabilized for improved light stability; Vicat/B 120 = 118 °C; UL recognition 94 V-0 at 1.5 mm |
Non-reinforced flame retardant grades |
| Bayblend® FR3030 | (PC+ABS)-blend; flame retardant; Vicat/B 120 tempe - rature = 115 °C; extrusion grade; good extrusion and vacuum-forming behavior; UL recognition 94 V-0 at 1.5 mm; halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 1.0 mm | |
| Bayblend® FR3040 | (PC+ABS)-blend; flame retardant; Vicat/B 120 tempera - ture = 108 °C; HDT/A >= 85 °C; for thin-wall applications; very good burning behavior in small wallthicknesses (UL recognition 94 V-0 at 0.75 mm and above and V-1 at 0.6 mm) | |
| Bayblend® FR1514 | (PC+ABS)-blend; flame retardant; high heat resistance; Vicat/B 120 temperature = 136 °C; ball indentation tem - perature >= 125 °C; UL recognition 94 V-0 at 1.5 mm; suitable as supporting material for energized parts | |
| Bayblend® FR1514 BBS073 | (PC+ABS)-blend; flame retardant; Vicat/B 120 tem - perature = 136 °C; improved chemical resistance and stress cracking behavior compared to KU2-1514; ball indentation temperature >= 125 °C; UL recognition 94 V-0 at 1.5 mm; suitable as supporting material for energized parts | |
| Bayblend® FR3020 | (PC+ABS)-blend; 5 % mineral filled; flame retardant; Vicat/B 120 temperature = 103 °C; HDT/A >= 85 °C; for thin-wall applications; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); low smoke density |
Mineral-filled flame retardant grades |
| Bayblend® FR3021 | PC+ABS)-blend; 15 % mineral filled; flame retardant; Vicat/B 120 temperature = 98 °C; high stiffness; tensile modulus = 4,800 MPa; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960 °C at 2.0 mm | |
| Bayblend® ET3032 FR | Rubber modified PC blend; 10 % mineral filled; flame retardant; Vicat/B 120 temperature = 108 °C; extrusion grade; good extrusion and vacuum-forming behavior; UL 94 V-0 (0.75 mm) (Covestro internal test); glow wire temperature (GWFI): 960 °C at 2.0 mm | |
| Bayblend® FR410 MT | Rubber modified PC blend; 10 % mineral filled; flame retardant; Vicat/B 120 temperature = 108 °C; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); for railway interiors; due to the special formulation of this grade, the final parts may require coating; | |
| Bayblend® FR411 MT | Rubber modified PC blend; flame retardant; mineral filled; Vicat/B 120 temperature = 99 °C; extrusion grade; for European railway interiors requiring EN45545; | |
| Bayblend® FR421 MT | Rubber modified PC blend; mineral filled; flame retardant; Vicat/B 120 temperature = 134 °C; extrusion grade for aircraft interiors; |
Resins wholesale,Factory-Direct supply,Certified supplier
Main Product: PC,PC/ABS,PC/PET,PC/PBT
Customized Services: Modified, Color matching, Production technical support
Several Warehouse: Guang zhou, Dong guan, Shen zhen, Hong kong
Contact Us at Any Time