Covestro PC Apec 1695 easy release
| Brand Name | Covestro |
| Model Number | 1695 |
Product Details
Payment & Shipping Terms
Minimum Order Quantity
25KG
Price
*USD to be negotiated
Packaging Details
25Kgs/BAG
Payment Terms
L/C, T/T, Western Union, MoneyGram
Product Description
Main physical property
Easy-flow grades / easy-release
MVR (330°C/2.16kg) 45 cm³/10 min; easy release; softening temperature (VST/B 120)=158 °C; injection molding - melt temperature 320 - 340°C; Covers for brake lights and indicator lights; Headlamp reflectors/bezels
Rheological properties
| Property | Test Condition | Unit | Standard | typical Value | |
| C | Melt volume-flow rate |
330 °C/ 2.16 kg
|
cm³/10 min | ISO 1133 |
45
|
|
Melt mass-flow rate
|
330 °C/ 2.16 kg
|
g/10 min
|
ISO 1133 |
46
|
|
| C |
Molding shrinkage, parallel
|
60x60x2 mm
|
% | ISO 294-4 |
0.75
|
| C |
Molding shrinkage,normal
|
60x60x2 mm
|
% | ISO 294-4 |
0.75
|
Mechanical properties (23 °C/50 % r. h.)
| Property | Test Condition | Unit | Standard | typical Value | |
| C | Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 2350 |
| C |
Yield stress
|
50 mm/min | MPa | ISO 527-1,-2 | 68 |
| C | Yield stress | 50 mm/min | % | ISO 527-1,-2 | 6.2 |
| C |
Nominal strain at break
|
50 mm/min | % | ISO 527-1,-2 |
>50
|
| C |
Charpy impact strength
|
23 °C | kJ/m² |
ISO 179/1eU
|
N |
| C |
Charpy impact strength
|
-30°C | kJ/m² |
ISO 179/1eU
|
N |
|
Flexural modulus
|
2 mm/min | MPa |
ISO 178
|
2400 | |
|
Flexural strength
|
2 mm/min | MPa |
ISO 178
|
100 | |
|
Ball indentation hardness
|
N/mm² |
ISO 2039-1
|
120 | ||
Resins wholesale,Factory-Direct supply,Certified supplier
Main Product: PC,PC/ABS,PC/PET,PC/PBT
Customized Services: Modified, Color matching, Production technical support
Several Warehouse: Guang zhou, Dong guan, Shen zhen, Hong kong
Get in Touch for More Info! and Speak to Our Manager Today!
Recommended Products
Contact Us at Any Time
+8618002579887
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong